MS2 Frequently Asked Questions針常問問題

Q. How much MS2 can I expect to use?問:有多少針我能期望用?

A; While exact usage depends on machine configuration and time of use per day on average you can assume that a machine generating between 2.5 and 3.0 Lbs of dross per hour will consume 1 liter of MS2 per 40 hours of operation.一;雖然確切用法取決於機器配置和使用時,每天平均你可以假設機發電之間的2.5倍和3.0磅的糟粕,每小時可消耗1升針,每40小時運作. One liter will usually reduce 45 Kg or 100 Lbs of dross back into useable solder.一公升通常會減少45公斤或100磅的糟粕放回可用焊料.

Q. How does MS2 work?問:如何針工作?

A. the active ingredients in the MS2 complexes with metal oxides in the solder bath dross and render them soluble in the bulk material.A的活性成分的針配合金屬氧化物的焊料浴糟粕,使其可溶性在散裝物料. This material is also unique in its dual role as a heat stable oxygen barrier and as an oxide scavenger.這種材料還具有獨特的雙重角色,作為熱穩定阻隔氧,作為氧清除劑. MS2l works with no discernible smoke or odor if used within normal solder pot temperatures.ms2l工程無辨別煙或異味,如果使用正常焊料鍋溫度. Right out of the bottle MS2 is non-toxic and non-irritating and the resulting spent organometallic waste presents no inhalation or contact hazard.右出瓶針,是無毒,無刺激性,因而用有機廢物列出吸入NO或接觸危險.

Q. Does MS2 mix with the solder?問:是否針混入焊料?

A. No. Not only do we know that because of the chemical formulation we have also confirmed this through numerous independent lab tests.答:不會.我們不但知道,因為化學制訂,我們也證實了這一點通過無數獨立的實驗室測試. Lab test data is available from P. KAY Metal.實驗室試驗數據,從第安基金屬.

Q. Does MS2 normally contact the assembly being soldered?問:是否針通常接觸的裝配焊接?

A. No, MS2 does not mix with the solder or travel over the wave.答:沒有,針不混入焊料或旅行的浪潮.

Q. How do I clean MS2 from a board or assembly if I mistakenly do so?問:我該如何清潔針,由董事會或組裝,如果我誤做?

A. MS2 can be removed from circuit boards with a solution of hot water and 4% Environ Gold 816 saponifier.甲餘2,可以從電路板,以解決熱水和4%環境金牌816皂.

Q. How do I clean MS2 from tools or machine components?問:我該如何清潔針從工具或機器零件?

A. MS2 can be removed from machine components or tools by cleaning with a towel while the item to be cleaned is still warm.甲餘2,可以從機器零件或工具的清潔用毛巾,而該項目是清洗仍然溫暖.

Q. Does MS2 corrode or have a detrimental effect on the materials that compose the solder pot?問:是否針腐蝕或有不利影響的物質組成焊料鍋?

A. No答:沒有

Q. Can MS2 be shipped by air?問:可以針空運運送?

A. Yes.答:是. There are no restrictions on shipping MS2 by any normal means.有沒有限制航運針任何正常手段.

Q. Is MS2 flammable?問:是易燃針?

A. No, MS2 is not flammable.答:沒有,針不易燃.

Q. Is MS2 conductive?問:是導電針?

A. MS2 is not applied to the board and leaves no detrimental residue so this is not normally a concern.餘甲2並不適用於董事會和留下任何有害殘留物等,這是不正常的關注. Extensive SIR testing has been performed through independent labs.先生廣泛的測試已經完成,通過獨立實驗室. It is not conductive in the fresh or unused condition. However, as it becomes spent it contains metal oxides and possibility flux residues that can be conductive.它是不導電的新鮮或閒置狀態.然而,因為它成了花它含有金屬氧化物和可能性通量殘留,可以導電. Of course, dross is also conductive.當然,糟粕也導電.

Q. What are the equipment manufacturer positions on MS2?問:什麼是設備製造商的立場針?

A. Most have no position just as they have no position regarding the brand of solder used.答:大部分沒有立場,只是因為他們沒有立場品牌焊錫用. We have had a comment that “Our machine does not generate dross so why would the customer use MS2?我們曾評論說:"我們的機器,不產生廢渣為什麼還要客戶使用針? If everyone used MS2 than our dross free machine would loose its advantage”.如果人人都用針比我們糟粕免費機將鬆散的優勢". Frankly we are still looking for that dross free wave solder machine.坦白說,我們仍在尋找其糟粕,波峰焊機.

Q. How should the small amount of MS2 be handled?問:應如何少量針如何處理?

A. While the amount of spent MS2 will equate to a tiny fraction of the dross that would have been generated there will be a few hundred milliliters per day of spent MS2 depending on production volumes.答:雖然這筆花費針將等同於一個很小的糟粕曾希望產生將有幾百毫升每天花針取決於生產量. The spent MS2 should be returned to P. KAY Metal or our distributors for return to an authorized recycling center.廢針應歸還頁安基金屬或直銷商返回特准回收中心.

Q. Is there any special labeling for spent MS2?問:是否有任何特殊標記用針?

A. Spent MS2 contains oxides of the metals that would be found in the specific solder pot therefore we recommend labeling it as you would dross甲花針含有氧化物中的重金屬,會發現在特定焊料鍋因此,我們建議標號為你會糟粕

Q. Is the spent MS2 considered hazardous?問:是用針視為有害?

A. As noted above, the spent MS2 contains oxides of the metals in your solder alloy therefore, for example, spent MS2 that has been used to eliminate dross in a leaded alloy will contain lead oxides and should be treated accordingly.答:如上所述,用針含有氧化物的金屬貴焊錫因此,舉例來說,花針,一直被用來消滅糟粕,在含鉛合金將含有氧化鉛和應相應處理.

Q. How is MS2 different from the powders and oils that have been used in the past?問:如何針不同於粉末和植物油中曾經使用過?

A. MS2 is a process chemical that not only inhibits dross formation but actually reduces dross back to its native metals as it forms.餘甲2是一個化學過程,不僅抑制其糟粕形成,但實際上是在減少糟粕回到了家鄉金屬,因為它的形式. There is no similarity of chemistry between the older materials and the new technology MS2.有沒有相似的化學之間的舊材料和新工藝的針.

Q. MS2 is not a low priced material, how can I calculate my savings when using it?問餘2不是一個低價位的材料,我怎麼計算我的積蓄在使用它?

A. A simple calculation is to determine how much 100 Lbs (45 Kg) of your solder costs as that is how much dross a liter of MS2 reduces back into useable metal.答:簡單的算術運算,以確定有多少100磅(45公斤),你焊料成本,因為這是多少糟粕一升針減少放回可用金屬. Deduct the cost of that much solder from your cost of one liter of MS2 and you will have a gross savings number.扣除成本,遠焊料從你的成本,一升針前,你將有總儲蓄額多少. This of course does not take into consideration the significant savings eliminating dross related rework and reducing maintenance as well as increasing throughput will save.這當然不考慮節省大量消除糟粕相關返工率和減少維修以及為增加貨物吞吐量將可節省. P. KAY metal has a savings calculator available for use on the Companies web site that you can use for a more precise calculation.第安基金屬儲蓄計算器可供利用公司網站,你可以使用更精確的計算.

Q. What is the shelf life of MS2?問:什麼是貨架壽命的針?

A. The shelf life is in excess of two years.A的貨架壽命超過兩年.

Q. Are there storage temperature limits while storing MS2?問:是否有貯藏溫度限制而存儲針?

A. The material should not be allowed to reach temperatures below 35 degrees F as some components may separate.A的材料不能達到溫度低於35華氏度,因為有些部件可以分開的. There is no practical upper limit to the material within all normally accepted storage conditions.有沒有實際的上限的物質,通常全部接納儲存條件. The material is stable at high temperatures.材料是穩定在較高的溫度下.

Q. Why is MS2 200LF so much more expensive and why does it not contain lead?問:為什麼是針200lf這麼昂貴得多,為什麼它不含有鉛?

A. The original formulation was optimized for lead free alloys.答:原來的提法是適合無鉛合金. It was thought that with lead free solders being so expensive that MS2 would find the most market acceptance in that area.據認為與鉛焊料被這麼昂貴,針會找到最市場接受這方面的工作. We soon found out that those using leaded solder had a great deal of interest in MS2 also.我們很快發現,那些使用含鉛焊錫產生了很大的興趣,也針. The price of the MS2 200 LF (for lead free) was to high for economical use with cheaper leaded alloys therefore a less pure version, one that did not have to be optimized for lead free RoHS compliant alloys was developed and offered to the market.價格的200針LF爐(無鉛),是高節約使用便宜的含鉛合金因此較為純淨版一,沒有進行優化無鉛封裝無鉛合金的發展,並提供給市場. MS2 200LF does not contain lead because it is purified differently than the 100Pb which will pick up lead in a cheaper quicker purification process.針200lf不含有鉛,因為它是純淨不同於100pb後將拿起鉛便宜快捷的淨化過程.

Q. I see that there is a carbonized ring visible on my solder pot after using MS2.問:我看到有一個環形炭化看得見我焊料鍋後,用針. Is this normal or harmful?這是正常還是有害?

A. This is normal.答:這是正常的. Dross is not a clean byproduct.糟粕都不是一場乾淨的副產品. MS2 is far less messy than dross but it can leave some residues which are easily reduced during normal maintenance.針遠低於較凌亂糟粕,但也留下一些殘渣很容易降低,因此在正常維修. The carbon ring or material that you see has no long term effects to your solder pot or process.碳環或材料,你看有沒有一個長遠的影響你的焊料壺或過程.

Q. what happens if we completely turn off our pots at the end of the day or for the weekend?問:什麼情況下,如果我們完全關掉鍋在結束一天或週末?

A. Letting the solder cool with the MS2 in place is not a problem unless the metal cools to the solid state.甲讓酷焊料與針到位不是問題,除非金屬冷卻到固態. When cooled to the point of being solid the metal can shrink away from the edges allowing MS2 to seep in between the metal and the walls of the solder pot.當冷卻到一點是固體金屬可縮小遠離邊緣,讓針滲中間的金屬和牆壁的焊錫鍋. While this will not harm the pot the trapped MS2 will temporally give some smoke while the pot is re heating.雖然這不會損害鍋被困針會暫時讓一些煙霧,而罐重暖氣. If the pot is allowed to cool to solid we recommend using a P. KAY metal supplied retainer ring or simply remove the MS2 until the pot heated to near operating temperature once again.如果鍋讓其冷卻固我們建議使用第一種安基金屬供應擋圈或只是清除了針,直到鍋加熱到接近運行溫度一次.